LNP™ THERMOCOMP™ RF00CSXP compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4kiSwG_LNP-THERMOCOMP-RF00CSXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* RF00CSXP is a compound based on Nylon 66 resin, containing Glass Fiber. Added features of this material include: Heat Stabilized Also known as: LNP* THERMOCOMP* Compound RF-100-12 HS Product reorder name: RF00CSXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 226 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 17500 | MPa | ISO 178 |
| Flexural Stress | 317 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 250 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7500 GF 35 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Cri-Line FDA-715 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Ferro PP NPP00GX08BK | Ferro Corporation | Polyolefin, Unspecified | Ferro PP |
| Electrafil® ABS CF15 BK | Techmer Engineered Solutions | ABS | Electrafil® |
| NHU-PPS 1230C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |