Marlex® HMN TR-935
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4k9G2f_Marlex-HMN-TR-935.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® HMN TR-935 is a Medium Density Polyethylene material. It is available in Latin America or North America for rotational molding. Important attributes of Marlex® HMN TR-935 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693A | ||
| 10% Igepal, Compression Molded, F50 | 130 | hr | |
| 100% Igepal, Compression Molded, F50 | > 1000 | hr | |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.17 mm, Rotational Molded) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.17 mm, Rotational Molded) | 750 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| 2% Secant : 3.17 mm, Rotational Molded | 620 | MPa | |
| Tangent : 3.17 mm, Rotational Molded | 760 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact | |||
| -40°C, 3.20 mm | 102 | J | |
| -40°C, 6.35 mm | 237 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.17 mm, Rotational Molded | 58.0 | °C | |
| 1.8 MPa, Unannealed, 3.17 mm, Rotational Molded | 41.0 | °C | |
| Brittleness Temperature | -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 128 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 112 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 GB 10 | RTP Company | Nylon 66 | RTP |
| SUPREME Specialty PS SP201 4551 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME Specialty PS |
| Evoprene™ GC 5701 | AlphaGary | SEBS | Evoprene™ GC |
| Geon™ Specialty Suspension Atlas S140 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Geon™ Vinyl Flexible B5546 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |