Sup-tech B9706
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4iyGlw_Sup-tech-B9706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sup-tech B9706 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 1.0E-3 to 5.0E-3 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.1 | % | |
| Saturation, 23°C | 6.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 140 | MPa | DIN 53455 |
| Tensile Strain (Break) | 2.0 | % | DIN 53452 |
| Flexural Modulus | 8000 | MPa | DIN 53457 |
| Flexural Stress | 190 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 185 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silmar® SIL08LH-70 | Interplastic Corporation | Polyester, TS | Silmar® |
| Unipren® Elastomers A3 NTLA010 70A UP303 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Capran® 518 LL | Honeywell | Nylon 6 | Capran® |
| Aropol™ RTM 80501 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |