GETILAN GPE/400 XT2
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4i8mRe_GETILAN-GPE-400-XT2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN GPE/400-D GRAFTING is a medium density chemically crosslinkable compound for low voltage power cables insulation andsheathing. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our type MAC/100 or MAC/202 red cupper resistant. REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify: IEC 502 XLPE, CEI 2011 G7 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.30 - 0.60 | g/10 min | ASTM D1238 |
| Water Absorption (100°C, 24 hr) | 0.60 | % | IEC 60811 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 430 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr 1 | 10 | % | IEC 60811 |
| 150°C, 168 hr 2 | 12 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr 3 | -5.0 | % | IEC 60811 |
| 150°C, 168 hr 4 | -17 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 5(250°C) | 45 - 60 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | BS 6622 |
| Additional Information |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by:-Immersion of the bobbin into hot water at 85/90 °C for some hours (up to 3 mm thickness).-Steam treatment at 0.15 for bar 5/6 hours.-Faster ambient curing is possible depending from the atmospheric conditions. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Die Temperature | 210 | °C |
| Note Message | |
|---|---|
| 1 . | Air Bomb |
| 2 . | Heat Aging |
| 3 . | Air Bomb |
| 4 . | Heat Aging |
| 5 . | 20N/cm2, Residual Value -5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| STARFLEX® P 7033-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Adstif HA801U | LyondellBasell Industries | PP Homopolymer | Adstif |
| Chemlon® A60XT | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Laticonther 57 CPG/550 | LATI S.p.A. | PPA | Laticonther |