Sup-tech A260
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4i1YgV_Sup-tech-A260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech A260 is a Polyamide 66 (Nylon 66) product filled with 30% mineral. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 8.0E-3 to 0.010 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.80 | % | |
| Saturation, 23°C | 6.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 8.0 | % | DIN 53452 |
| Flexural Modulus | 5600 | MPa | DIN 53457 |
| Flexural Stress | 115 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 243 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C | |
| Melting Temperature | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 6.0 to 10 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BC10BK6549 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Boda BDF60C | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| ELASTEL™ AF-1 | HELLENIC CABLES S.A. | EVA | ELASTEL™ |
| LNP™ LUBRICOMP™ KFI15 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| Hostacom X 437 S 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |