AKROLOY® PA GF 50 black (2706)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4hn0w9_AKROLOY-PA-GF-50-black-2706-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 50 black (2706) is a 50% glass fibre reinforced polyamide-blend with very high stiffness and strength, even in conditioned state. Applications are components with high dimensional stability, independent from moisture content. AKROLOY PA GF 50 black is an alternative for aluminium- and zinc diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.59 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 9.00 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 54.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | < 0.30 | -- | % | |
| Water Absorption (Saturation, 23°C) | 3.5 to 4.0 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.1 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 110 to 130 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 140 to 150 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 290 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17500 | 16500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | 220 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16400 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 17 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 110 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 242 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 255 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.5E+17 | -- | ohms | IEC 60093 |
| Volume Resistivity | 9.1E+13 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.42 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Epoxies, Ect. 10-3008 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Kepamid® 2340GF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ LUBRICOMP™ MAP41XXP compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ LUBRICOMP™ |
| LUVOCOM® 1-0889-2 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| Sylvin 9915-87UV Red 6283 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |