ALCUDIA® LDPE 2107F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4hEDtS_ALCUDIA-LDPE-2107F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 3235F is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown film applications. This material offers easy processability and good balance of mechanical properties. TYPICAL APPLICATIONS
Recommended melt temperature range from 160 to 190°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 500 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 4.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PC 1010F-T5 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Huafon HF-1275AP | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Hybrid S570 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| LUVOCOM® 1105/GY7993 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| OmniLon™ PA6/6 U IM20 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |