LNP™ LUBRICOMP™ RCL36 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4goAhm_LNP-LUBRICOMP-RCL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RCL36 is a compound based on Nylon 66 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wesr Resistant, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound RCL-4036 Product reorder name: RCL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.72 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 32400 | MPa | ASTM D638 |
| -- | 22600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 182 | MPa | ASTM D638 |
| Break | 245 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 0.90 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 18400 | MPa | ASTM D790 |
| -- | 22700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 372 | MPa | ASTM D790 |
| -- | 396 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor - Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 69 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Taitalac® 8540H | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| DINALEN® 30 | DIOKI d.d. | LDPE | DINALEN® |
| LNP™ THERMOCOMP™ LC006E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| POCAN® B 3225 000000 | LANXESS GmbH | PBT | POCAN® |