ColorFast® PCGF110
| Category: | PC , Polycarbonate |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4g82PI_ColorFast-PCGF110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High modulus 10% glass-filled polycarbonate, V2-rated, general purpose |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 66.2 | MPa | |
| Break | 55.2 | MPa | |
| Tensile Elongation 2(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 3 | 3450 | MPa | ASTM D790 |
| Flexural Strength 4 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 142 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baypreg® 400 | Covestro - PUR | PUR-MDI | Baypreg® |
| Flontech® FT-915-RSL | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hapflex™ 669-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Sylvin 9995-68 Blue 8486 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DC006ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |