ULTEM™ 2210F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4em9LY_ULTEM2210Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.55 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6900 | MPa | ASTM D638 |
| -- | 6800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 139 | MPa | ASTM D638 |
| Yield | 140 | MPa | ISO 527-2/5 |
| Fracture 3 | 140 | MPa | ASTM D638 |
| Fracture | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/5 |
| Fracture | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 5 | 6890 | MPa | ASTM D790 |
| -- 6 | 6500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 210 | MPa | ISO 178 |
| Yield, 50.0mm span 7 | 227 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 9 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 13.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 211 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 226 | °C | ASTM D1525 10 |
| -- | 212 | °C | ISO 306/B50 |
| -- | 218 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 3013A | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Tefzel® 280 | DuPont Fluoropolymers | ETFE | Tefzel® |
| Axiall PVC 21572 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Sylvin 8482-72 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Sylvin 9077-75 Grey 9516 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |