Visico™ LE4423/Ambicat™ LE4472 Datasheet,XLPE,Borealis AG-SHANGHAI SUSHENG

Visico™ LE4423/Ambicat™ LE4472

Category:	XLPE , Crosslinked Polyethylene
Manufacturer:	Borealis AG
Trademark:	Visico™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4eXbIZ_Visico-LE4423-Ambicat-LE4472.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Visico LE4423 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables. The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water. When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico LE4423 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,5% of fine size carbon black ensuring excellent weatherability. Visico LE4423 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico LE4423 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst. Visico LE4423 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure: ANSI/ICEA S-70-547 ASTM D 1248 Type II, Class C, Category 4 HD 603 S1 HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9) IEC 60502-1 NEMA WC 70 NEMA WC 71 The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information. The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4472 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4423 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane.

Message

Visico LE4423 / Ambicat LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables.

The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4472 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.

When properly mixed, addition of 7 parts of Ambicat LE4472 to 93 parts of Visico LE4423 , insulation with excellent thermo-oxidative stability, also in contact with copper as will as aluminium, is achieved. The final product will contain nominal 2,5% of fine size carbon black ensuring excellent weatherability.

Visico LE4423 / Ambicat LE4472 contains antioxidant, metal deactivator and a drying agent. Visico LE4423 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.

Visico LE4423 / Ambicat LE4472 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure:

ANSI/ICEA S-70-547

ASTM D 1248 Type II, Class C, Category 4

HD 603 S1

HD 626 S1 (TIX-2, TIX-4, TIX-6, TIX-9)

IEC 60502-1

NEMA WC 70

NEMA WC 71

The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information.

The base material Visico LE4423 in combination with the catalyst masterbatch Ambicat LE4472 is a ready-made two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. Visico LE4423 is based upon a cost optimised low density polyethylene, copolymerised with vinyl silane.

General Information
Additive	Antioxidant Carbon Black (3%) Metal Deactivator Scorch Resistant
Features	Antioxidant Crosslinkable Fast Cure Good Processability Good Surface Finish Good Thermal Stability Good Weather Resistance Oxidation Resistant
Uses	Power Cable Jacketing Wire & Cable Applications
Agency Ratings	ANSI/ICEA S-70-547 ASTM D 1248, II, Class C, Cat. 4 HD 603 S1 IEC 60502-1 NEMA WC-70 , WC-71
Appearance	Black
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density ¹	0.933	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (Condition B, 50°C, 10% Igepal, F20)	> 96.0	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	52		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 15.0	MPa	ISO 527-2/250
Tensile Strain (Break)	> 300	%	ISO 527-2/250

Aging	Nominal Value	Unit	Test Method
Change in Tensile Properties - 240 hr (135°C)	< 25	%	IEC 60811-1-2

Thermal	Nominal Value	Unit	Test Method
Hot Set			IEC 60811-2-1
200°C ²	60	%
200°C ³	0.0	%

Additional Information	Nominal Value	Unit
Crosslinking
700.0 µm ⁴	1.5	day
700.0 µm ⁵	< 15.0	min
1.80 mm ⁶	7.0	day
1.80 mm ⁷	1.00	hr

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Electric Strength	> 20	kV/mm	IEC 60243-1
Dielectric Constant (50 Hz)	< 2.50		IEC 60250
Dissipation Factor (50 Hz)	< 6.0E-4		IEC 60250

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150	°C
Cylinder Zone 2 Temp.	170	°C
Cylinder Zone 3 Temp.	170	°C
Cylinder Zone 4 Temp.	170	°C
Die Temperature	170	°C

Note Message
1 .	Mixture 93:7, ISO 1872-2
2 .	Elongation under load, 0.20 MPa
3 .	Permanent deformation, 0.20 MPa
4 .	In air 23°C, 50 % humidity
5 .	90°C, Sauna or water bath
6 .	In air 23°C, 50 % humidity
7 .	90°C, Sauna or water bath

Resin Grade	Manufacturer	Category	Trademark
Quantum Composites QC-8704	Quantum Composites Inc.	Vinyl Ester	Quantum Composites
Toyolac® 100 MPF	Toray Plastics (Malaysia) Sdn. Bhd.	ABS	Toyolac®
TUFNYL® SGF 40 NATURAL	SRF Ltd.	Nylon 6	TUFNYL®
YUZEX® 8800U	SK Global Chemical	HDPE	YUZEX®
MARPOL® EVA 1707	Marco Polo International, Inc.	EVA	MARPOL® EVA

Resin Grade

Manufacturer