SABIC® PPcompound 8611A resin
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4eKBRQ_SABIC-PPcompound-8611A-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8611A is a mineral filled, impact modified polypropylene TPO. It was originally designed for painted automotive bumper fascia applications where a combination of low density, good flow, high stiffness, and cold temperature ductility is required. The IMDS is 482236460. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.968 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C, 1 hr | 1.1 | % | |
| Across Flow : 120°C, 30 min | 1.1 | % | |
| Across Flow : 23°C, 48 hr | 0.95 | % | |
| Flow : 80°C, 1 hr | 0.60 | % | |
| Flow : 120°C, 30 min | 0.71 | % | |
| Flow : 23°C, 48 hr | 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 19.0 | MPa | ISO 527-2/50 |
| Break | 13.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm Span) | 1760 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 6.0 | kJ/m² | |
| 23°C 3 | 34 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| 0°C | 30 | kJ/m² | |
| 23°C | 41 | kJ/m² | |
| Instrumented Dart Impact 5 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 24.0 | J | |
| 23°C, Energy at Peak Load | 22.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 49.0 | µm/Mk | |
| Transverse : -30 to 100°C | 127 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 2.20 m/sec |
| 6 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novamid® 1030J | DSM Engineering Plastics | Nylon 6 | Novamid® |
| AKROMID® B3 GF 35 black (2196) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DURANEX® 361SA | Polyplastics Co., Ltd. | ABS+PBT | DURANEX® |
| LEXAN™ EXL8134 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Petrothene® LT570401 | LyondellBasell Industries | HDPE | Petrothene® |