Stanyl® 46HF5040
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4e3Ugt_Stanyl-46HF5040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® 46HF5040 is a Polyamide 46 (Nylon 46) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Stanyl® 46HF5040 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.77 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.30 | -- | % | |
| Flow | 0.90 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 15000 | 12000 | MPa | |
| 120°C | 9500 | -- | MPa | |
| 160°C | 6500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 190 | 130 | MPa | |
| Break, 120°C | 100 | -- | MPa | |
| Break, 160°C | 85.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 1.7 | 2.5 | % | |
| Break, 120°C | 3.0 | -- | % | |
| Break, 160°C | 3.0 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 13000 | 11000 | MPa | |
| 120°C | 8500 | -- | MPa | |
| 160°C | 5500 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 14 | kJ/m² | |
| 23°C | 13 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 50 | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | 15 | kJ/m² | |
| 23°C | 15 | 15 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ||||
| Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flow | 1.7E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Transverse | 4.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Transverse | 6.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (0.350 mm) | 130 | -- | °C | UL 746 |
| Thermal Index - 5000 hrs | 163 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 325 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.250 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 300 to 315 | °C | |
| Front Temperature | 300 to 315 | °C | |
| Nozzle Temperature | 300 to 310 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® EX02 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Rigid | SILVER® |
| 4DUR® 9K22117 FR1 | 4Plas | PBT | 4DUR® |
| Nypol® PA B3 G30 UV HS NTLA010 NT311 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Biffa r-HDPE FOOD GRADE | Biffa Polymers Ltd | HDPE | Biffa |
| Andur 8-APF-LM/Curene® 3005 | Anderson Development Company | PUR-Ester/TDI | Andur |