RTP 2800 D-55A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4ddqYT_RTP-2800-D-55A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade." |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 2.2 to 2.6 | % | ASTM D955 |
| Moisture Content | < 0.040 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 50% Strain, 3.18 mm | 1.38 | MPa | |
| 100% Strain, 3.18 mm | 1.90 | MPa | |
| 300% Strain, 3.18 mm | 3.45 | MPa | |
| Tensile Strength 2(Yield, 3.20 mm) | 4.65 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 700 | % | ASTM D412 |
| Tear Strength 4 | 30.6 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 17 | % | |
| 70°C, 168 hr | 44 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (125°C, 168 hr) | 1.7 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (125°C, 168 hr) | 7.7 | % | ASTM D573 |
| Change in Durometer Hardness in Air (125°C, 168 hr) | 0.0 | ASTM D573 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 193 to 227 | °C | |
| Mold Temperature | 10.0 to 79.4 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | Die C, 510 mm/min |
| 2 . | Die C, 500 mm/min |
| 3 . | Die C, 500 mm/min |
| 4 . | Die C |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 SI 2 | RTP Company | Nylon 66 | RTP |
| Ming Dih EPS S2-211 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Next Nylon 66 Prime Series PG30-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Clear-Flex® 50 | Smooth-On, Inc | PUR, Unspecified | Clear-Flex® |
| INSULCAST® 333/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |