VESTAMID® HTplus M3033
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4dXQHc_VESTAMID-HTplus-M3033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAMID HTplus M3033 is a PA 10T-based, black colored, glass-fiber reinforced (30%), heat-stabilized copolyamide. PA 10T is a poly-condensation product of 1,10-decamethylene diamine (10) and terephthalic acid (T). As 1,10-decamethylene diamine is derived from castor oil plants, VESTAMID HTplus M3033 is partially natural resourced and thus bio-based. Compared to PA 6T-based resins VESTAMID HTplus M3033 has a broader processing window as well as a reduced tendency to absorb water. Therefore the material exhibits less variation in mechanical properties and dimensional changes with humidity. This resin is especially suited for manufacturing parts subjected to high temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 169 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 7.5 | kJ/m² | |
| 23°C, Complete Break | 8.6 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 52 | kJ/m² | |
| 23°C, Complete Break | 56 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 284 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 263 | °C | ISO 75-2/A |
| Melting Temperature 1 | 285 | °C | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | > 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| RTP 4002 TFE 10 | RTP Company | PPA | RTP |
| Scolefin 54 H 14-0 | Ravago Group | PP Homopolymer | Scolefin |
| Sarlink® TPE TPE EE-2240N-01 | Teknor Apex Company | TPE | Sarlink® TPE |
| Orgalloy® RS 6635A | Arkema | Nylon 66 Alloy | Orgalloy® |