Next Nylon 66 Prime Series PG33-01ABK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4bkXB8_Next-Nylon-66-Prime-Series-PG33-01ABK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Black Compound Product Applications Generally recommended for Automotive industries, under the hood application manufacturer for component electric tools transport & building etc Benefits Excellent Balance with Mechanical & Thermal properties high creep resistance, and very good heat stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.28 | -- | % | ASTM D955 |
| Transverse flow | 0.75 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.5 | -- | % | ASTM D570 |
| Saturation 1 | 5.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 190 | 140 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 12500 | 9500 | MPa | ASTM D790 |
| Flexural Strength | 280 | 210 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -30°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 140 | 190 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 256 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | 26 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0334C10L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| ADDILENE H 442 M30 | ADDIPLAST | PP Homopolymer | ADDILENE |
| FHR Polypropylene P4G4K-205 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Durethan® BKV 15 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Indothene HD HD55EF010 | Reliance Industries Limited | HDPE | Indothene HD |