LUVOCOM® 1-8934/BL/L Datasheet,Nylon 66,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1-8934/BL/L is a polyamide 66 (nylon 66) material, and the filler is glass fiber reinforced material. This product is available in Europe,. LUVOCOM®The main features of 1-8934/BL/L are: High stiffness high strength Creep resistance Typical application areas include: engineering/industrial accessories textile/fiber Tools Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Rigidity, high High strength Good creep resistance
Uses	Textile applications Non-specific food applications Engineering accessories Machine/mechanical parts Application in Automobile Field Business equipment Cam Mold/Mold/Tool
Appearance	Blue

Physical	Nominal Value	Unit	Test Method
Density	1.61	g/cm³	ISO 1183
Molding Shrinkage	0.30 - 0.60	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10100	MPa	ISO 527-2
Tensile Stress (Break)	135	MPa	ISO 527-2
Tensile Strain (Yield)	2.9	%	ISO 527-2
Flexural Modulus	8600	MPa	ISO 178
Flexural Stress	208	MPa	ISO 178
Flexural Strain at Flexural Strength	4.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	160	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+9	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	73	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	120	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+9	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Drying Time
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	290 - 310	°C
Middle Temperature	290 - 310	°C
Front Temperature	290 - 310	°C
Nozzle Temperature	280 - 300	°C
Processing (Melt) Temp	290	°C
Mold Temperature	90.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4bPlFu_LUVOCOM-1-8934-BL-L.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TIPPLEN® H 145 F	MOL Petrochemicals Co. Ltd.	PP Homopolymer	TIPPLEN®
NYLEM® 66 GFR 35	EMAS Plastik San.Tic.AS.	Nylon 66	NYLEM®
Geon™ Vinyl Flexible BP90W2	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Osterlene® PPH-20-.9-NA	Osterman & Company	PP Homopolymer	Osterlene®
Plaslube® POM CO AF15	Techmer Engineered Solutions	Acetal (POM) Copolymer	Plaslube®