TECHNYL® A 218HP V50 BLACK 21 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4bKHgI_TECHNYL-A-218HP-V50-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218HP V50 Black 21 N is a polyamide 66, reinforced with 50% of glass fibre, heat stabilized, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.52 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ||||
| Across Flow | 0.90 | -- | % | ISO 294-4 |
| Across Flow | 0.50 | -- | % | Internal Method |
| Flow | 0.30 | -- | % | Internal Method |
| Molding Shrinkage Isotropy | 0.600 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15000 | 10500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 200 | 143 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 13500 | -- | MPa | ASTM D790 |
| -- | 13500 | 10000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 280 | -- | MPa | ASTM D790 |
| -- | 320 | 230 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | 94 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 200 | -- | J/m | ASTM D256 |
| 23°C | 20 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 80 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 253 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7PAN (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ASTAMID™ MB3M6 | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| Gallonprene® GP310-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| PLUSTEK PA201 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| POLYfill PPC K5025 | Polykemi AB | PP Copolymer | POLYfill |