LNP™ THERMOCOMP™ HB006 compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4bIpzG_LNPTHERMOCOMPHB006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP HB006 is a compound based on Nylon 11 resin containing Glass Bead. Also known as: LNP* THERMOCOMP* Compound HB-1006 Product reorder name: HB006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.7 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.5 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.5 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1970 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.5 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Fracture | 43.4 | MPa | ASTM D638 |
| Fracture | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 23 | % | ASTM D638 |
| Yield | 24 | % | ISO 527-2 |
| Fracture | 20 | % | ASTM D638 |
| Fracture | 43 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1920 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 3 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 33.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 145 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 151 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 46.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 47.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Task® 12 | Smooth-On, Inc | PUR, Unspecified | Task® |
| Cheng Yu A707G25 | Cheng Yu Plastic Company Limited | SAN | Cheng Yu |
| Latishield 73/13-07A | LATI S.p.A. | Acetal (POM) Copolymer | Latishield |
| Teldene® B07ML | National Petrochemical Industries Company (NATPET) | PP Impact Copolymer | Teldene® |
| Sarlink® TPE ME-2245N (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |