BLUESTAR® PBT 403M-G20
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Nantong Zhonglan Engineering Plastics Co., Ltd. |
| Trademark: | BLUESTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4b85Ne_BLUESTAR-PBT-403M-G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BLUESTAR® PBT 403M-G20 is a Polybutylene Terephthalate (PBT) product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 to 1.58 | g/cm³ | ASTM D792 |
| Ash Content | 20.0 to 24.0 | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus 3 | 6800 | MPa | ASTM D790 |
| Flexural Strength 4 | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 5.50 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) (23°C) | 48.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 195 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (in oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (50 Hz) | 3.40 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 0.020 | ||
| 60 Hz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Nozzle Temperature | 240 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa | |
| Back Pressure | 6.00 to 18.0 | MPa | |
| Screw Speed | < 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E4008 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Sylvin 7833-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LOTTMER SE-064AN | Lotte Chemical Corporation | SEBS | LOTTMER |
| POLYblend PC/ABS 45FS GKF2010 | Polykemi AB | PC+ABS | POLYblend |
| Sylvin 7833-85 Grey 9596 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |