ASTALAC™ ABS 2147
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4a6PxF_ASTALAC-ABS-2147.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALAC™ ABS 2147 is an extrusion packaging grade developed for improved resistance to stress cracking and excellent tear resistance, particularly for thermoformed lids. It is designed for low temperature applications in contact with aggressive food stuffs. Underwriters Laboratory Reference E183535-B. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 0.80 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 35 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 56.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 200 - 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Top Roll Temperature: 60 to 80°C Middle Roll Temperature: 70 to 90°C Bottom Roll Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1382 TFE 5 | RTP Company | PPS | RTP |
| THERMOLAST® K TP5CDZ (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| WPP PP PPHFGC-3 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Celcon® M140 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Sylvin 3270-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |