LNP™ LUBRICOMP™ Noryl_NWR5810 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Zg2Eo_LNP-LUBRICOMP-Noryl-NWR5810-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP NORYL_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.55 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.45 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2170 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 39.3 | MPa | |
| Break | 37.9 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.8 | % | |
| Break | 55 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 4 | 2070 | MPa | |
| 100 mm Span 5 | 2000 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 50.0 mm Span 6 | 61.4 | MPa | |
| Yield, 100 mm Span 7 | 57.2 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 230 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2200 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 32.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 113 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 117 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 97.2 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 106 | °C | |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 8 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 60°C | 6.5E-5 | cm/cm/°C | |
| Transverse : -40 to 60°C | 7.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 98.9 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 227 to 277 | °C | |
| Middle Temperature | 238 to 282 | °C | |
| Front Temperature | 249 to 288 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E General Purpose G-4285UV | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| TABOREX TA 1135 HD | SILON s.ro | HDPE | TABOREX |
| Aaroprene® ATPO 3000 50D | Aaron Industries Corp. | TPO (POE) | Aaroprene® |
| ESENTTIA 01R25 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Pibiter® NRV20 NAT001 | SO.F.TER. SPA | PBT | Pibiter® |