BioCeres® BC-LBI08
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FuturaMat |
| Trademark: | BioCeres® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4ZeA3w_BioCeres-BC-LBI08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC-LBI08 is an agromaterial descending from the BioCérès range. It is a wheat flour-based product. BC-LBI08 is 100% biodegradable and from renewable ressources. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 to 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 12 to 36 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 70 to 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1510 to 2090 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 to 16.0 | MPa | |
| Break | 7.00 to 13.0 | MPa | |
| Tensile Strain (Yield) | 0.80 to 1.4 | % | ISO 527-2 |
| Flexural Modulus | 1680 to 3120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 6.0 to 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 45.0 to 53.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4705 FR | RTP Company | PTT | RTP |
| AKROMID® C3 ICF 30 5 XTC black (5473) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| Hostaform® SXT90Z-01 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| IDI SMC S42 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Lupolen 4261A IMBD | LyondellBasell Industries | HDPE, HMW | Lupolen |