LubriOne™ AT-000/05T NATURAL

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	PolyOne Corporation
Trademark:	LubriOne™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4ZSrBD_LubriOneAT00005TNATURAL.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PTFE lubricated POM compound

General Information
Features	Low friction coefficient Copolymer Good wear resistance Lubrication
Uses	Gear Conveyor accessories Industrial application Roller Pulley Home appliance components Application in Automobile Field Business equipment Consumer goods application field Printing machine parts Bearing
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.43	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.5 - 2.5	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	58.0	MPa	ASTM D638
Flexural Modulus ²	2300	MPa	ASTM D790
Flexural Strength ³	75.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm, Injection Molded)	53	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm)	96.0	°C	ASTM D648

Flammability	Nominal Value		Test Method
Flame Rating			UL 94
1.5 mm	HB		UL 94
3.0 mm	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80 - 90	°C
Drying Time	2.0 - 3.0	hr
Processing (Melt) Temp	180 - 200	°C
Mold Temperature	75 - 85	°C

Note Message
1 .	Type 1, 50mm/min
2 .	1.3 mm/min
3 .	1.3 mm/min

Resin Grade	Manufacturer	Category	Trademark
Sylvin 6177-85 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
SUPREME Specialty PS SP6520	Supreme Petrochem Ltd.	PS (Specialty)	SUPREME Specialty PS
Ultra Purge HT	Moulds Plus International USA, Inc.	Proprietary	Ultra Purge
Paracril OZO® 3341	INSA	PVC+NBR	Paracril OZO®
ExxonMobil™ LLDPE LL 1001 Series	ExxonMobil Chemical	LLDPE	ExxonMobil™ LLDPE