Braskem PE LD7000A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Z6kcx_Braskem-PE-LD7000A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LD7000A is a Low Density Polyethylene produced by High Pressure Process, in Autoclave reactor. Developed for the manufacturing of extruded films. It has high mechanical and impact strength, good processability, high ESCR and good shrinkage. Application: Heavy-duty bags; agriculture, coextruded and shrink films; blow molding; tubes and hoses. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.34 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 280 | % | |
| TD : Break, 38 µm, Blown Film | 880 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 130 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 18 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1000-GF30 | QTR, Inc. | PC | QR Resin |
| Starex GR-4030 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Cheng Yu FV30715 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Karina GRAY PVC COMPOUND 801-18/215-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLIMAXX 2564PCXTA6 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |