RTP 485 TFE 15
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Z0w42_RTP-485-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Compressive Strength | 82.7 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.16 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 130 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 116 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.79 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 50 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 1mil/in.Wear Factor, K, ASTM D-3702: 25E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.16The wear factor and coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| BMC 5209 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| DynaStat® 2257 | Polymer Dynamix | Nylon 12 | DynaStat® |
| Plaslube® PC / PBT IM 5230 | Techmer Engineered Solutions | PC+PBT | Plaslube® |
| LG ABS XR418 | LG Chem Ltd. | ABS | LG ABS |