MARPOL® LL6S 801
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4YcR9u_MARPOL-LL6S-801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: MARPOL® LL6S 801 is a linear low density polyethylene film resin. Films made from this Super Strength hexene copolymer exhibit excellent tear and impact strength. Recommended Applications: Blown film extrusion and blown stretch wrap film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 165 | MPa | |
| 1% Secant, TD | 186 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 8.96 | MPa | |
| TD : Yield | 9.65 | MPa | |
| MD : Break | 62.7 | MPa | |
| TD : Break | 51.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 630 | % | |
| TD : Break | 720 | % | |
| Dart Drop Impact | 330 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 460 | g | |
| TD | 600 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 37 | ASTM D2457 | |
| Haze | 17 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P30B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| CompaDur® 121 black (018) | DimeLika Plast GmbH | PBT | CompaDur® |
| Duratuf™ 830 | Technical Polymers, LLC | Acetal (POM) Copolymer | Duratuf™ |
| Karina WHITE PVC COMPOUND -E820-10/133-Y-ERYB (E-76534) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax CB 1160 G1 C11538 | LyondellBasell Industries | PP Copolymer | Hifax |