ElectriPlast® EP-CF/PP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4XNLTT_ElectriPlast-EP-CF-PP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-CF/PP is a polypropylene product that contains nickel-plated carbon fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | < 1.00 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5370 | MPa | ASTM D638 |
| Tensile Strength (Break) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 4120 | MPa | ASTM D790 |
| Flexural Strength | 43.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 118 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | 23 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 10 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 20 | mm/min | UL 94 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 249 | °C | |
| Middle Temperature | 254 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 1.24 | MPa | |
| Screw Speed | 185 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 300 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell PP RR-32 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Axiall PVC 10870 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DILAMID® 6 FV BLACK 3136 | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| Elastron® V V201.D40.B | Elastron USA, Inc. | TPV | Elastron® V |
| LOXIM 215 01 V0 | LOXIM Industries Private Limited | PBT | LOXIM |