Sarlink® TPE FM-2166 Datasheet,TPE,Teknor Apex Company-SHANGHAI SUSHENG

Message
Sarlink TPE FM-2166 is a general purpose thermoplastic elastomer, available in NAT, BLK, and colors, designed for various applications in the transportation industry including automotive floor mats. Sarlink TPE FM-2166 is a medium hardness, high density, UV stabilized grade that exhibits excellent wear resistance, low fogging and is suitable for injection molding and extrusion.

General Information
Features	Low to No Fogging High specific gravity High density smoothness Good UV resistance Workability, good Good adhesion Low liquidity Good chemical resistance Good wear resistance Lubrication Fill Medium hardness
Uses	Application in Automobile Field Car interior parts
RoHS Compliance	RoHS compliance
Appearance	Black Grey Available colors Natural color brownish yellow
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	5.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Test Method
Durometer Hardness		ISO 868
Shore A, 1 second, injection molding	68	ISO 868
Shore A, 5 seconds, injection molding	66	ISO 868
Shore A, 15 seconds, injection molding	64	ISO 868

Mechanical	Nominal Value	Unit	Test Method
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel)	181	mg	SAE J948

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ISO 37
Transverse flow : 100% strain	1.74	MPa	ISO 37
Flow : 100% strain	2.07	MPa	ISO 37
Tensile Stress ²			ISO 37
Transverse flow : Fracture	5.70	MPa	ISO 37
Flow : Fracture	5.00	MPa	ISO 37
Tensile Elongation ³			ISO 37
Transverse flow : Fracture	740	%	ISO 37
Flow : Fracture	640	%	ISO 37
Tear Strength ⁴			ISO 34-1
Transverse flow	24	kN/m	ISO 34-1
Flow	25	kN/m	ISO 34-1
Compression Set ⁵			ISO 815
23°C, 22 hr	24	%	ISO 815
70°C, 22 hr	51	%	ISO 815
90°C, 70 hr	88	%	ISO 815

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air			ISO 188
Lateral flow : 80°C, 1000 hr ⁶	24	%	ISO 188
Traffic : 80°C, 1000 hr ⁷	19	%	ISO 188
Lateral flow : 100% strain 80°C, 1000 hr ⁸	1.5	%	ISO 188
Traffic : 100% strain 80°C, 1000 hr ⁹	2.5	%	ISO 188
Transverse flow : 110°C, 1008 hr ¹⁰	6.3	%	ISO 188
Flow : 110°C, 1008 hr ¹¹	5.6	%	ISO 188
Transverse flow : 100% strain 110°C, 1008 hr ¹²	4.1	%	ISO 188
Flow : 100% strain 110°C, 1008 hr ¹³	6.0	%	ISO 188
Transverse flow : 125°C, 168 hr ¹⁴	10	%	ISO 188
Flow : 125°C, 168 hr ¹⁵	8.1	%	ISO 188
Transverse flow : 100% strain 125°C, 168 hr	-1.8	%	ISO 188
Flow : 100% strain 125°C, 168 hr ¹⁶	0.80	%	ISO 188
Change in Tensile Strain at Break in Air ¹⁷			ISO 188
Lateral flow : 80°C, 1000 hr	1.3	%	ISO 188
Traffic : 80°C, 1000 hr	3.9	%	ISO 188
Transverse flow : 110°C, 1008 hr	2.2	%	ISO 188
Flow : 110°C, 1008 hr	5.3	%	ISO 188
Transverse flow : 125°C, 168 hr	14	%	ISO 188
Flow : 125°C, 168 hr	19	%	ISO 188
Change in Shore Hardness in Air			ISO 188
Shao A, 80°C, 1000 hr ¹⁸	0.10		ISO 188
Shao A, 80°C, 1000 hr ¹⁹	0.60		ISO 188
Shao A, 80°C, 1000 hr ²⁰	0.80		ISO 188
Shao A, 110°C, 1008 hr ²¹	3.2		ISO 188
Shao A, 110°C, 1008 hr ²²	3.4		ISO 188
Shao A, 110°C, 1008 hr ²³	3.6		ISO 188
Shao A, 125°C, 168 hr ²⁴	0.20		ISO 188
Shao A, 125°C, 168 hr ²⁵	0.60		ISO 188
Shao A, 125°C, 168 hr ²⁶	0.70		ISO 188

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -60.0	°C	ASTM D746

Flammability	Nominal Value	Unit	Test Method
Burning Rate	38	mm/min	ISO 3795

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	167	Pa·s	ASTM D3835

Additional Information	Nominal Value	Unit	Test Method
Volatiles			SAE J1756
Fogging, 3 hrs @ 100°C, 21°C Plate 16 hrs post	92	%	SAE J1756
Atomization, 3 hours, 100°C,21°C plate = 93%	94	%	SAE J1756
Tear Strength			ISO 34-1
1000 hrs @ 80°C (Across Flow)	12	%	ISO 34-1
1000 hrs @ 80°C (Flow)	8.3	%	ISO 34-1

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	199 - 210	°C
Middle Temperature	204 - 216	°C
Front Temperature	210 - 221	°C
Nozzle Temperature	216 - 227	°C
Processing (Melt) Temp	216 - 227	°C
Mold Temperature	35 - 66	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Fast
Back Pressure	0.172 - 0.862	MPa
Screw Speed	50 - 120	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	193 - 204	°C
Cylinder Zone 2 Temp.	199 - 210	°C
Cylinder Zone 3 Temp.	204 - 216	°C
Cylinder Zone 4 Temp.	204 - 216	°C
Cylinder Zone 5 Temp.	210 - 221	°C
Die Temperature	216 - 227	°C

Extrusion instructions
螺杆转速30 - 100 rpm

Note Message
1 .	Type 1, 510mm/min
2 .	Type 1, 510mm/min
3 .	Type 1, 510mm/min
4 .	B method, right angle specimen (without cut), 510mm/min
5 .	Type a
6 .	Type 1
7 .	Type 1
8 .	Type 1
9 .	Type 1
10 .	Type 1
11 .	Type 1
12 .	Type 1
13 .	Type 1
14 .	Type 1
15 .	Type 1
16 .	Type 1
17 .	Type 1
18 .	1 sec
19 .	5 sec
20 .	15 sec
21 .	1 sec
22 .	5 sec
23 .	15 sec
24 .	1 sec
25 .	5 sec
26 .	15 sec

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Sarlink® TPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4X3npM_SarlinkTPEFM2166.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Silopren® LSR 4670	Momentive Performance Materials Inc.	Silicone Rubber, LSR	Silopren®
Smoothblend® PC-1201	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	PC	Smoothblend®
THERMOLAST® K TC4GPN (Series: GP/FG)	KRAIBURG TPE	TPE	THERMOLAST® K
Ultralloy™ 306	Hapco Inc.	TP, Unspecified	Ultralloy™
MAJORIS ET460 - 8487	AD majoris	PP, Unspecified	MAJORIS