Sylvin 6231-90 Red 6302
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Sylvin Technologies Incorporated |
| Trademark: | Sylvin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4VO0DE_Sylvin623190Red6302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sylvin 6231-90 Red 6302 Is A Vinyl Compound Formulated For Jacketing Applications That Require Superior Flammability And Chemical Resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 90 | ASTM D2240 | |
| Shaw A, 10 seconds | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 330 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 105 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 105 | °C | ASTM D794 |
| Brittleness Temperature | -10.0 | °C | ASTM D746 |
| Melting Temperature | 177 - 188 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 ZRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| TAFMER™ A-35070S | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| Taitacell EPS-361MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| AKROMID® A3 GF 35 3 black (1802) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| LinGen FR345 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |