Network Polymers PP PPB 25 1503 GF10
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4V7oih_Network-Polymers-PP-PPB-25-1503-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers PP PPB 25 1503 GF10 is a Polypropylene Copolymer (PP Copolymer) product filled with 10% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 8.7 | % | ASTM D638 |
| Flexural Modulus 4 | 1690 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 150 | J/m | ASTM D256A |
| Gardner Impact (-20°C) | 1.92 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 91.1 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellidor CP 2825-11 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| HiFill® PBT 1225 L BK | Techmer Engineered Solutions | PBT | HiFill® |
| KEBAFORM® C 903 LF | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LNP™ THERMOCOMP™ LC004XXP compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |
| Dryflex® SE 70A301 | ELASTO | TPE | Dryflex® |