HiFill FR® PA6/6 GF25 FR-N IM
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4UpVL3_HiFill-FR-PA6-6-GF25-FR-N-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR® PA6/6 GF25 FR-N IM is a Polyamide 66 (Nylon 66) product filled with 25% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 99.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 120 | J/m | |
| 23°C | 220 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 229 | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 550 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | > 6.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4M 850 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| RIALFILL H 15 SL 50 TC | RIALTI Srl | PP Homopolymer | RIALFILL |
| Sylvin 2931-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Absolac® 140 | Styrolution | ABS | Absolac® |
| FMC® 205 | Smooth-On, Inc | Polysulfide Rubber | FMC® |