Iupiace® TX403
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4RFwGN_Iupiace-TX403.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupiace® TX403 is a Polyphenylene Ether + PS (PPE+PS) material filled with filler. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupiace® TX403 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 51.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.6 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 24 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 26 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4175 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SWANCOR Epoxy 976 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| BP HDPE 9610 R BLK | Buckeye Polymers, Inc. | HDPE | BP |
| KOCETAL® WR303BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Mablex SA966 | Ravago Group | PC+ABS | Mablex |