Vyncolit® 2061B Datasheet,Epoxy,Vyncolit N.V.-SHANGHAI SUSHENG

Message
Vyncolit 2061B is an epoxy; The epoxy resin material contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. The main features of Vyncolit 2061B are: flame retardant/rated flame chemical resistance low viscosity Heat resistance Typical application areas include: food contact applications Electrical/electronic applications military applications

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	The degassing effect is low to no Low viscosity Solvent resistance Anti-salt water/fog Good thermal shock resistance Good chemical resistance alkali resistance acid resistance Non-corrosive
Uses	Electrical components Military application
Agency Ratings	FDA not rated USDA Unspecified Approval
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.95	g/cm³	ASTM D792
Bulk Factor	2.5		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.30 - 0.50	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	70		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	55.2	MPa	ASTM D638
Flexural Modulus	14500	MPa	ASTM D790
Flexural Strength	131	MPa	ASTM D790
Compressive Strength	214	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	35	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	149	°C	ASTM D648
CLTE - Flow	4.2E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.54	W/m/K	ASTM C177
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength ¹	13	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	3.50		ASTM D150
Dissipation Factor (1 MHz)	0.019		ASTM D150
Arc Resistance	180	sec	ASTM D495

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	V-0		UL 94
Oxygen Index	45	%	ASTM D2863

Injection	Nominal Value	Unit
Middle Temperature	60.0 - 82.2	°C
Nozzle Temperature	82.2 - 93.3	°C
Processing (Melt) Temp	104 - 116	°C
Mold Temperature	135 - 177	°C
Injection Pressure	34.5 - 68.9	MPa
Holding Pressure	13.8 - 34.5	MPa
Back Pressure	0.345	MPa

Injection instructions
Gauge: 0.3The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.2%Dielectric Strength, ASTM D149, 60 Hz, Method B, wet: 320 V/milDielectric Constant, ASTM D150, 1000000 Hz, wet: 3.5Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.019Bulk Factor, ASTM D1895: 2 to 3Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 220 °F Mold Temperature: 250 to 530 °F Compression Mold Pressure: 200 to 1500 psi Transfer Mold Pressure: 100 to 2000 psi Cure Time, 0.125 in: 75 sec

Injection instructions

Gauge: 0.3The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.2%Dielectric Strength, ASTM D149, 60 Hz, Method B, wet: 320 V/milDielectric Constant, ASTM D150, 1000000 Hz, wet: 3.5Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.019Bulk Factor, ASTM D1895: 2 to 3Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 220 °F Mold Temperature: 250 to 530 °F Compression Mold Pressure: 200 to 1500 psi Transfer Mold Pressure: 100 to 2000 psi Cure Time, 0.125 in: 75 sec

Note Message
1 .	Method B (step by step)

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	4Qmld5_Vyncolit-2061B.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
PROTEQ™ C16UST2Z	Marplex Australia Pty. Ltd.	PP Copolymer	PROTEQ™
SCHULATEC® PEEK MV 14	A. Schulman Europe	PEEK	SCHULATEC®
InnoTuf® HP-2190A	Innovative Polymers, Inc.	TSU	InnoTuf®
Karina CLEAR PVC COMPOUND -E 80/206-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Lusin® Clean L 52 F	Chem-Trend L.P.	Unspecified	Lusin®