Amodel® A-1565 HS
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4QHmOu_Amodel-A-1565-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AMODEL A- 1565 HS is a polyphthalamide (PPA) reinforced 65% glass fiber and mineral fiber. It is mainly aimed at high cost-effective products that require high rigidity, good dimensional stability and good rigidity at high temperatures. The brand has both high deformation temperature and bending modulus. -black: A- 1565 HS BK 324 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.90 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | ASTM D955 |
| Transverse flow | 0.50 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| -- | 20700 | 20800 | MPa | ASTM D638 |
| 23°C | 19700 | -- | MPa | ISO 527-2 |
| 100°C | 15400 | -- | MPa | ISO 527-2 |
| 150°C | 5720 | -- | MPa | ISO 527-2 |
| 175°C | 5100 | -- | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Fracture, 23°C | 138 | -- | MPa | ISO 527-2 |
| Fracture, 100°C | 91.7 | -- | MPa | ISO 527-2 |
| Fracture, 150°C | 46.2 | -- | MPa | ISO 527-2 |
| Fracture, 175°C | 32.4 | -- | MPa | ISO 527-2 |
| -- | 131 | 123 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Fracture | 1.2 | 1.2 | % | ASTM D638 |
| Fracture, 23°C | 1.0 | -- | % | ISO 527-2 |
| Fracture, 100°C | 1.3 | -- | % | ISO 527-2 |
| Fracture, 150°C | 2.4 | -- | % | ISO 527-2 |
| Fracture, 175°C | 1.8 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 17900 | 18000 | MPa | ASTM D790 |
| 23°C | 9100 | -- | MPa | ISO 178 |
| 100°C | 6830 | -- | MPa | ISO 178 |
| 150°C | 2480 | -- | MPa | ISO 178 |
| 175°C | 2280 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 210 | 196 | MPa | ASTM D790 |
| 23°C | 211 | -- | MPa | ISO 178 |
| 100°C | 163 | -- | MPa | ISO 178 |
| 150°C | 69.6 | -- | MPa | ISO 178 |
| 175°C | 55.8 | -- | MPa | ISO 178 |
| Compressive Strength (13.0 mm) | 189 | -- | MPa | ASTM D695 |
| Shear Strength | 71.0 | 49.6 | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.4 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -- | 37 | 32 | J/m | ASTM D256 |
| 23°C | 4.0 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ||||
| -- | 410 | -- | J/m | ASTM D256 |
| 23°C | 32 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 271 | -- | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 311 | -- | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ASTM E831 | |||
| Flow : 0 to 100°C | 2.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow : 100 to 200°C | 1.7E-5 | -- | cm/cm/°C | ASTM E831 |
| Lateral : 0 to 100°C | 3.7E-5 | -- | cm/cm/°C | ASTM E831 |
| Lateral : 100 to 200°C | 8.1E-5 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 4.0E+14 | -- | ohms·cm | ASTM D257 |
| Arc Resistance | 125 | -- | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | -- | V | UL 746 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.045 | % | |
| Hopper Temperature | 79.4 | °C | |
| Rear Temperature | 304 - 318 | °C | |
| Front Temperature | 316 - 329 | °C | |
| Processing (Melt) Temp | 321 - 343 | °C | |
| Mold Temperature | 135 | °C |
| Injection instructions |
|---|
| Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANTEX® 257C | Nantex Industry Co., Ltd. | SBR, Unspecified | NANTEX® |
| DINAPLEN® PPH1S07 G30 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| GAPEX® RPP30EB80HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Hifax TYC 852P E G12808 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 5150-80 Brown 7309 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |