Promyde® BF33
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4QGP5a_Promyde-BF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® BF33 is a medium viscosity Polyamide 6 used in simultaneous biaxial orientated film. CHARACTERISTICS Promyde® BF33 combines good gas barrier properties with chemical resistance, good mechanical and optical properties, high abrasion resistance and good thermoformability. APPLICATIONS Promyde® BF33 is a medium viscosity lubricated Polyamide 6 used in simultaneous biaxial orientated film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.69 | g/cm³ | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 9.0 | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | % | |
| Extractables | < 1.0 | % | ISO 6427 |
| Moisture Content 2 | < 0.10 | % | Internal Method |
| Relative Viscosity 3(25°C) | 3.21 to 3.41 | ISO 1628 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission - 85% RH (23°C) | 15 | g/m²/24 hr | ISO 15106-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Chip Size 4 | 2.50 | mm | Internal Method |
| Dynamic Friction Coefficient - Film/Steel | < 0.250 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 50 µm | 34.0 | MPa | |
| Break, 50 µm | 96.0 | MPa | |
| Tensile Elongation - MD (Break, 50 µm) | 350 | % | ISO 527-3 |
| Trouser Tear Resistance - MD (50 µm) | 25.0 | N/mm | ISO 6383-1 |
| Oxygen Transmission Rate | ASTM D3985 | ||
| 23°C, 0% RH, 50 µm | 25 | cm³/m²/24 hr | |
| 23°C, 50% RH, 50 µm | 15 | cm³/m²/24 hr | |
| 23°C, 85% RH, 50 µm | 40 | cm³/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 50.0 µm 5 | < 0.50 | % | |
| 50.0 µm 6 | < 5.0 | % |
| Note Message | |
|---|---|
| 1 . | NAPPA-059 |
| 2 . | NAPPA-032 |
| 3 . | 1% m/v in 96% m/m sulfuric acid |
| 4 . | NAPPA-045 |
| 5 . | Chill roll temperature 50°C |
| 6 . | Chill roll temperature 90°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3499-3 X 113393 C | RTP Company | LCP | RTP |
| SABIC® LDPE 2200H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Formolene® 6610A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Idemitsu PS SEHI-125 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| INLUBE PA66CF20TF15 | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |