TECHNYL® C 548B BLACK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4OqtAo_TECHNYL-C-548B-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 548B Black is an unreinforced polyamide 6, high viscosity, for extrusion blow-moulding. This product is available in black color. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal method | |||
| Vertical flow direction | 1.3 | -- | % | Internal method |
| Flow direction | 1.2 | -- | % | Internal method |
| Water Absorption (23°C, 24 hr) | 1.2 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.960 | -- | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 500 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 55.0 | 45.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 150 | -- | % | ISO 527-2/1A |
| Flexural Modulus | 1750 | 850 | MPa | ISO 178 |
| Flexural Stress | 70.0 | 45.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 20 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 92 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 90 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | -- | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.12 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Cylinder Zone 1 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 240 | °C | |
| Adapter Temperature | 220 - 240 | °C | |
| Die Temperature | 215 - 235 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 220 to 240°CBlow Molding Mold Temperature: 40 to 60°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8802 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| VITAMIDE® AT36NT6214 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Xuchuan XCS-2035DC | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| INLUBE PA66GF20TF15 | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |
| Magnobond 65 | Magnolia Plastics, Inc. | Epoxy | Magnobond |