Borealis PP EH105AEB
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4OSb3G_Borealis-PP-EH105AEB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EH105AEB is a 10% mineral filled elastomer modified polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 36 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Flexural Stress | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 51 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 83.0 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/Ae |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Tmperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 35HNF50-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| TOTAL Polyethylene HDPE XT10 N | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| Ultramid® A3EG7 BK23189 | BASF Corporation | Nylon 66 | Ultramid® |
| EverGlide® MB5230P | Polymer Dynamix | PE, Unspecified | EverGlide® |
| DISTRUMID 6 HI LT | Distrupol | Nylon 6 | DISTRUMID |