Sup-tech H706
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Nk0XX_Sup-tech-H706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech H706 is a Polyamide 46 (Nylon 46) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 5.0E-3 to 8.0E-3 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 2.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 200 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 8200 | MPa | DIN 53457 |
| Flexural Stress | 280 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 280 | °C | |
| 1.8 MPa, Unannealed | 240 | °C | |
| Melting Temperature | 295 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 24 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 9.0 to 18 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP ERTACETAL® H | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Moplen EP3307 | PolyMirae | TPO (POE) | Moplen |
| Yanshan PE 7600M | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| ELASTOSIL® AUX PRIMER G 3243 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| Petlon Prime A1-G15-00-NT | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |