Order Products : sales@su-jiao.com
Softflex® 0826
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Softflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Nff0D_Softflex-0826.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Softflex 0826 is suitable for overmolding ABS, PC, ABS/PC and PPO. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg 1 | 8.5 | g/10 min | |
| 235°C/1.0 kg | 8.0 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 44 to 50 | ||
| Shore A, 10 sec | 38 to 44 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 5.65 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-22 Wheel) | 44.0 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (100% Strain) | 7 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 0.834 | MPa | |
| 100% Strain | 1.23 | MPa | |
| 300% Strain | 2.22 | MPa | |
| Tensile Strength (Yield) | 7.11 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 740 | % | ASTM D412 |
| Tear Strength | 25.4 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact (-30°C) | > 36.2 | J | ASTM D5420 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 to 60.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 160 to 182 | °C | |
| Middle Temperature | 171 to 193 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 216 | °C | |
| Processing (Melt) Temp | 193 to 210 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Injection Pressure | 34.5 to 41.4 | MPa | |
| Holding Pressure | 27.6 to 31.0 | MPa | |
| Back Pressure | 0.517 to 1.03 | MPa | |
| Screw Speed | 20 to 40 | rpm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6926 AF 017 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Santoprene™ 8221-65M300 | ExxonMobil Chemical | TPV | Santoprene™ |
| BESTNYL SI00VI12BWX | Triesa Plastics | Nylon 6 | BESTNYL |
| Hax™ HF 217 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Huafon JF-P-5175 / JF-I-5118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |