Matrixx FPP5A20CC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4MriVF_Matrixx-FPP5A20CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Matrixx FPP5A20CC is a polypropylene material, and the filler is 20% glass fiber reinforced material. This product is available in North America,. The main features of the Matrixx FPP5A20CC are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 44.1 | MPa | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with Matrixx test methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 199 - 243 | °C | |
| Middle Temperature | 199 - 243 | °C | |
| Front Temperature | 199 - 243 | °C | |
| Processing (Melt) Temp | 199 - 243 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | < 0.345 | MPa | |
| Screw Speed | 20 - 60 | rpm | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Drying not normally required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEALUTION™ 230 Peel Polymer | The Dow Chemical Company | POP | SEALUTION™ |
| Sicoflex S454 | Ravago Group | ABS | Sicoflex |
| LNP™ VERTON™ RVL29 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| MAJORIS ET307 - 8584 | AD majoris | PP, Unspecified | MAJORIS |
| 3M™ Dyneon™ PTFE Compound PDR 06014 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |