ACRYLITE® Sheet FF
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4LWCqF_ACRYLITE-Sheet-FF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® extruded is the highest quality continuously manufactured sheet on the market today. Using a proprietary, innovative process, ACRYLITE® extruded sheet products are economical, provide tight thickness tolerance, high optical characteristics and low stress levels. ACRYLITE® extruded sheet is readily available in a variety of standard sizes, thicknesses and colors. ACRYLITE® extruded is a lightweight, rigid and weather-resistant thermoplastic that is dimensionally stable, resistant to breakage and can be easily fabricated and cemented. Because of its virtually distortion-free clarity, it is well suited for use in a variety of applications.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ASTM D785 | |
| Barcol Hardness | 48 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Compressive Strength | 117 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.6 | °C | ASTM D648 |
| Continuous Use Temperature | 71.1 | °C | |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat (25°C) | 1460 | J/kg/°C | |
| Thermal Conductivity | 0.19 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(3.18 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.60 | ||
| 1 kHz | 3.30 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 0.060 | ||
| 1 kHz | 0.040 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.18 mm) | 25 | mm/min | ASTM D635 |
| Self Ignition Temperature | 454 | °C | ASTM D1929 |
| Smoke Density | 4.8 | % | ASTM D2843 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Forming Temperature | 149 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 881 TFE 5 | RTP Company | Acetal (POM) Copolymer | RTP |
| Veroplas ASG33 | PlastxWorld Inc. | SAN | Veroplas |
| Beamset 371 | Arakawa Chemical Industries, Ltd. | Epoxy | Beamset |
| APEX® 90-A471R-60-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| COPYLENE® CM200LN | Phillips 66 | PP Impact Copolymer | COPYLENE® |