VESTAKEEP® 4000G
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAKEEP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4LGtdS_VESTAKEEP-4000G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High-viscosity, unreinforced polyether ether ketone VESTAKEEP 4000G is a high-viscosity, unreinforced polyether ether ketone for injection molding and extrusion. The semi-crystalline polymer features superior thermal and chemical resistance. Parts made from VESTAKEEP 4000G are self-extinguishing. VESTAKEEP 4000G can be processed by common machines for thermoplastics. We recommend a melt temperature between 370°C and 380°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 180°C, 2.00 mm | 1.1 | % | |
| Flow : 180°C, 2.00 mm | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 96.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 30 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 6.0 | kJ/m² | |
| 23°C, Complete Break | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 335 | °C | ISO 306/A |
| -- | 305 | °C | ISO 306/B |
| Melting Temperature (DSC) 2 | 340 | °C | ISO 3146 |
| CLTE - Flow (23 to 55°C) | 6.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3 | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | ||
| 1 MHz | 2.80 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A 4 | 175 | V | |
| Solution A | 200 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 370 to 380 | °C | |
| Mold Temperature | 160 to 200 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 100 to 120 | °C | |
| Cylinder Zone 1 Temp. | 350 to 380 | °C |
| Note Message | |
|---|---|
| 1 . | determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 2 . | 2nd heating |
| 3 . | K20/P50 |
| 4 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS HF-3 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| VITAMIDE® BF23OR6570 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Uravin™ 901-65FR | Vi-Chem Corporation | PVC Alloy | Uravin™ |
| SQUARE® LIM2012-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| XENOY™ 1760E resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |