Generic Nylon 66 - Glass\Mineral
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4KPI33_Generic-Nylon-66---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 - 1.48 | g/cm³ | ASTM D792 |
| 23°C | 1.35 - 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.88 | % | ASTM D955 |
| 23°C | 0.39 - 1.2 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.59 - 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 120 - 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5960 - 12300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 82.7 - 120 | MPa | ASTM D638 |
| Yield, 23°C | 67.5 - 138 | MPa | ISO 527-2 |
| Fracture, 23°C | 114 - 152 | MPa | ASTM D638 |
| Fracture, 23°C | 118 - 170 | MPa | ISO 527-2 |
| 23°C | 116 - 139 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 1.9 - 3.1 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 5.2 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6490 - 7020 | MPa | ASTM D790 |
| 23°C | 3750 - 12500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 146 - 228 | MPa | ASTM D790 |
| 23°C | 100 - 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.8 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 32 - 66 | J/m | ASTM D256 |
| 23°C | 2.8 - 7.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 251 - 258 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 250 - 251 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 - 241 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 - 243 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 - 258 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 254 - 265 | °C | |
| -- | 260 | °C | DSC, ISO 3146 |
| CLTE - Flow | 1.6E-5 - 3.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.0E+2 - 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 3.5 - 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 398 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.0 - 90.0 | °C | |
| Drying Time | 2.9 - 5.1 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 264 - 302 | °C | |
| Middle Temperature | 277 - 294 | °C | |
| Front Temperature | 276 - 288 | °C | |
| Nozzle Temperature | 279 - 288 | °C | |
| Processing (Melt) Temp | 270 - 298 | °C | |
| Mold Temperature | 69.4 - 100 | °C | |
| Injection Pressure | 6.89 - 87.6 | MPa | |
| Back Pressure | 0.341 - 0.521 | MPa | |
| Screw Speed | 60 - 76 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 861.3 | RTP Company | Acetal (POM) Homopolymer | RTP |
| Anjacom® R250-H/GF15 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Sylvin 83033-75 Grey 9491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TC7HFZ (Series: UV/HF/SF) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Durethan® BKV 130 H2.0 DUS008 901510 | LANXESS GmbH | Nylon 6 | Durethan® |