TAROMID B 280 K10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4GnyYd_TAROMID-B-280-K10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 50% glass beads, good dimensional stability, good surface finish and good mechanical and thermal properties. Available: all colors, UV-stabilized (L), heat-stabilized (H), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 to 1.57 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.80 to 0.90 | % | ASTM D570, ISO 62 |
| Saturation | 5.5 | % | ASTM D570 |
| Saturation, 23°C | 5.5 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 80.0 | MPa | |
| Break | 75.0 | MPa | |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 114 | MPa | ISO 178 |
| Break | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 3.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 18 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 30 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 3 | 80.0 | °C | |
| -- 4 | 120 | °C | |
| Vicat Softening Temperature | 206 | °C | ISO 306/A50, ASTM D1525 5 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 20 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 550 | V | |
| Solution B | 250 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Short Term |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2590A | Teknor Apex Company | TPE | Telcar® |
| SolVin 271PC | INOVYN | PVC, Unspecified | SolVin |
| 4MID® 9B22130 FR1 | 4Plas | Nylon 6 | 4MID® |
| AKROTEK® PK-HM GF 30 natural (4709) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |
| Kotex K-40UVR | Kotec Corporation | PC | Kotex |