ULTEM™ 1285 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4GhmLc_ULTEM1285resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact compliant in recognized colors. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (320°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 110 | MPa | ISO 527-2/5 |
| Yield | 115 | MPa | ISO 527-2/50 |
| Fracture | 75.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/5 |
| Yield | 6.5 | % | ISO 527-2/50 |
| Fracture | 36 | % | ISO 527-2/5 |
| Fracture | 14 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 3250 | MPa | ISO 178 |
| Flexural Stress | 155 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 36.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 170 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 158 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 177 | °C | ISO 306/B50 |
| -- | 180 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.4E+16 | ohms | IEC 60093 |
| Volume Resistivity | 6.6E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.98 | IEC 60250 | |
| 60 Hz | 2.98 | IEC 60250 | |
| 1 MHz | 2.94 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.6E-3 | IEC 60250 | |
| 60 Hz | 2.6E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 300 - 330 | °C | |
| Mold Temperature | 95.0 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 25 NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Boda BDF-LB2701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| ARC ARC6608 | ARC Resin Corporation | Nylon 66 | ARC |
| Eastar™ DN004, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| LNP™ COLORCOMP™ HF1110RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |