LNP™ THERMOCOMP™ LF002 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Ggrd0_LNP-THERMOCOMP-LF002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF002 is a compound based on Polyetheretherketone resin containing 10% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1002 Product reorder name: LF002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6080 | MPa | ASTM D638 |
| -- | 6500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 120 | MPa | ASTM D638 |
| Yield | 125 | MPa | ISO 527-2/5 |
| Break 3 | 114 | MPa | ASTM D638 |
| Break | 122 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.4 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/5 |
| Break 5 | 4.2 | % | ASTM D638 |
| Break | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6010 | MPa | ASTM D790 |
| -- 7 | 5670 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 203 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 9 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 860 | J/m | ASTM D4812 |
| 23°C 10 | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.80 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 326 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 285 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 169 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 171 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVALON® 80 ABX | Huntsman Corporation | TPU-Polyester | AVALON® |
| Leona™ FG173 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Loyblend® TA-1002 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| PHOENIX™ 2551 | Phon Tech Industrial Company | SEBS | PHOENIX™ |
| OTECH TPO OTR7788-Molding | OTECH Corporation | TPE | OTECH TPO |