MAJ'ECO CG264BS
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4FWNGl_MAJ-ECO-CG264BS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO CG264BS is a glass fibre reinforced Biopolymer compound intended for injection moulding. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.0 | % | Internal method |
| Flow direction | 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 59.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3450 | MPa | ISO 178 |
| Flexural Stress 2 | 99.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 170 - 210 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1006 HI | RTP Company | PBT | RTP |
| SUMIKASUPER® LCP E6808LHF | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| HYBRAR™ 7311 | Kuraray Co., Ltd. | TPE | HYBRAR™ |
| LNP™ STAT-KON™ DX04490 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| EVALENE® PP PHT0171 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |