NYCOA Polyamide 4212 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4DiYCW_NYCOA-Polyamide-4212-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 4212 HS is a high viscosity resin particularly suitable for extrusion processing, thermoforming and blow molding. Its melt viscosity and strength provide ease of processing for sheet, profile, and blow molded articles. This material is specifically engineered for applications requiring high stiffness, impact strength, dimensional stability, and a greater service life than standard grades of glass reinforced Nylon 6. NYCOA 4212 HS is also available in UV stable grades as well as custom colors. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Suggested applications include thermoformed under the hood automotive components and blow molded chemical storage reservoirs. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 42 | % | ASTM D638 |
| Flexural Modulus 3 | 2210 | MPa | ASTM D790 |
| Flexural Strength 4 | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 260 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 190 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 169 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 238 - 249 | °C | |
| Middle Temperature | 249 - 266 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Nozzle Temperature | 260 - 277 | °C | |
| Processing (Melt) Temp | 254 - 271 | °C | |
| Mold Temperature | 65.6 - 76.7 | °C | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NMS1-01 S.GY. | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Evermore PUR SS-150BHR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| HANWHA CLNA TR-8142EC | Hanwha Chemical | LDPE | HANWHA |
| Zytel® ST811HS NC010 | DuPont Performance Polymers | Nylon 6 | Zytel® |
| Durethan® B 40 FA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |