SABIC® COHERE™ 8108L
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® COHERE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4DSCur_SABICCOHERE8108L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® COHERE™ 8108L is a ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose blown film applications and has excellent melt flow characteristics. SABIC® COHERE™ 8108L does contain Slip and Antiblock. Applications Typical application for SABIC® COHERE™ 8108L is low temperature seal packaging and lamination film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.908 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 970 | MPa | ASTM D882 |
| 1% secant, TD | 1080 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 460 | MPa | ASTM D882 |
| TD : Fracture | 550 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 540 | % | ASTM D882 |
| TD : Fracture | 640 | % | ASTM D882 |
| Dart Drop Impact 1 | > 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD | 20 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 105 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 6.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V150-72A | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Titacon® MS904 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Yanshan PE LD369 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Fluorosite 600 - GML | UNIFLON | PTFE | Fluorosite |
| Karina COMP. PVC CRYSTAL -E 57/201-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |